【摘要】环氧改性沥青混凝土具有比普通沥青混凝土优异得多的物理、力学性能,如高强度、优良的抗疲劳性能、良好的耐久性及抗老化性能,是受力特性异常复杂的正交异性钢桥面铺装、超重载交通道路、城市道路交叉口、公共汽车停靠站等特殊路段的理想材料,但由于环氧树脂和固化剂的不可逆反应,其施工要求非常严格。针对这一问题,本文结合实际工程对环氧沥青的施工温度、施工时间、碾压以及接缝的处理进行了研究,提出了关键工序中的控制指标和相关的控制方法。
【关键词】环氧改性沥青；施工控制；关键工序

【Abstract】Epoxy-modified asphalt concrete has a much more superior than conventional asphalt concrete physical, mechanical properties, such as high strength, excellent fatigue properties, good durability and anti-aging properties, is subject to very complex orthogonal force characteristics heterosexual steel bridge deck pavement, overweight containing roads, or urban road intersections, bus stops and other special sections of the ideal material, but because of epoxy resin and curing agent is not reversible reaction, and its construction very strict requirements. To solve this problem, The article, the actual construction works on the epoxy asphalt temperature, construction time, the processing of rolling, as well as joint research, put forward in the control of key process indicators and related control methods.
【Key words】Epoxy modified asphalt; Construction control; Key process
        1. 前言
        钢桥面铺装技术一直是一个施工难题，技术条件要求异常苛刻。在行车动载、风载、温度变化及地震等因素影响下，其高温稳定性、抗疲劳开裂性、对钢桥面板变形的追从性、层间粘结及完善的防排水体系等均有极高的要求。直接铺设在正交异性钢板上的桥面铺装材料,其受力和变形远较公路路面或机场道面复杂，因而对其强度、变形稳定性、疲劳耐久性等提出了的更高要求。
        环氧沥青一般由环氧树脂及固化剂两个部分组成。其固化反应使沥青性质从热塑性转变为热固性，因此环氧沥青有比普通沥青优异得多的物理、力学性能，如高强度、优良的抗疲劳性能、良好的耐久性及抗老化性能，是受力特性异常复杂的正交异性钢桥面铺装、超重载交通道路的理想材料；同时由于其极优良的粘结性能而应用于路面磨耗层，特别是需要较高抗磨耗性的寒冷地区路面。
        2. 工程概况
        湛江海湾大桥位于粤西的湛江地区，起于湛江市坡头区，于湛江市平乐渡口上游1.3Km处跨越麻斜海湾；湛江海湾大桥全长3981.17m，主桥为双塔双索面混合梁斜拉桥，主桥斜拉桥全长840.0316m，跨径组成为60m+120m+480m+120+60m 。根据湛江海湾大桥施工图设计文件，拟采用环氧沥青混凝土作为湛江海湾大桥钢桥面铺装方案。由于环氧沥青混凝土桥面通过了实验室的成功测试，而且该材料在国外的桥梁及国内的南京长江二桥等桥面上运行良好，随后又在南京长江三桥桥面铺装设计试验中得到进一步改进，因此，湛江海湾大桥也采用与南京三桥类